Contact lens treatment solution

ABSTRACT

The present invention is a contact lens treatment solution containing the following copolymer A and copolymer B in a ratio of A/B=40/1 to 5/1 (by weight). According to the present invention, there can be provided a contact lens treatment solution capable of removing dirt having adhered to contact lens surfaces, capable of improving lubricity of contact lens surfaces and capable of imparting persisting hydrophilicity to contact lens surfaces, by simple immersion treatment. 
     Copolymer A: a copolymer obtained by copolymerization of a monomer (a) represented by formula (1) and a monomer (b) represented by formula (2), in which the copolymerization ratio of the monomer (a) to the monomer (b), a/b=7/3 to 9/1 (by mol), and having a weight-average molecular weight of 400,000 to 800,000.
 
Copolymer B: a copolymer obtained by copolymerization of a monomer (a) represented by the formula (1) and a monomer (b) represented by the formula (2), in which the copolymerization ratio of the monomer (a) to the monomer (b), a/b=2/1 to 8/1 (by mol), and having a weight-average molecular weight of 1,000,000 to 1,500,000.

TECHNICAL FIELD

The present invention relates to a contact lens (CL) treatment solution. More precisely, the present invention relates to a CL treatment solution that can remove dirt having adhered to CL, simultaneously can improve the lubricity of CL surfaces, and can impart persisting hydrophilicity to CL surfaces, and relates to CL treated with the CL treatment solution.

BACKGROUND ART

Generally in wearing contact lenses, dirt of proteins, lipids and others derived from tear glands, eye discharges, sebum, cosmetics and the like may be often deposited thereon, and such dirt may often worsen the wearability, lower the corrected eyesight, and cause infectious diseases. Therefore, various measures against CL dirtiness have been developed.

As approaches heretofore taken for removing dirt having adhered to CL, a method of washing CL with a detergent that contains a surfactant, an oxidizing agent and a polishing agent is widely used. Further, as typified by PTL 1, a method of adding an enzyme to a CL detergent to efficiently remove dirt from CL is also widely used. In these approaches, the essential theme is to remove dirt having adhered to CL, which, however, could not attain a sufficient effect in prevention of dirt adhesion to CL.

As opposed to this, an approach of hydrophilizing CL surfaces is known as an approach for preventing dirt adhesion to CL. For example, PTL 2 proposes a method of hydrophilizing the surface of CL, using a solution that contains a phosphorylcholine group-containing polymer. However, the essential theme of the method is to prevent adhesion of dirt to CL, by which, therefore, a sufficient effect in removing dirt having adhered to CL could not be attained.

As an approach of satisfying both removal of dirt having adhered to CL and prevention of dirt adhesion to CL, PTL 3 proposes a CL treatment solution that contains a phosphorylcholine group-containing polymer, an alkylamide polyoxyethylene ether sulfate salt, and a hydrolase in a specific ratio. Using the treatment solution, dirt of proteins and lipids can be removed, and additionally adsorption of dirt of proteins and lipids can be prevented by imparting hydrophilicity to CL surfaces.

Further recently, a technique of imparting lubricity to CL surfaces has become desired in addition to the above-mentioned prevention of dirt adhesion to CL and removal of dirt having adhered to CL. Lubricity is said to be an important parameter for improving wearability of CL (for example, NPL 1).

CITATION LIST Patent Literature

-   PTL 1: JP 1-180515 A -   PTL 2: JP 7-166154 A -   PTL 3: JP 2000-147442 A

Non-Patent Literature

-   NPL 1: M. Roba et. at, “Tribol. Lett.”, 2011, Vol. 44, pp. 387-397

SUMMARY OF INVENTION Technical Problem

The CL treatment solution described in the above-mentioned PTL 3 could be effective to a certain extent for prevention of dirt adhesion to CL and for removal of dirt having adhered to CL, but there still remains room for improvement of lubricity impartation to CL surfaces and of persistence of hydrophilicity (persisting hydrophilicity) given to CL surfaces.

An object of the present invention is to provide a CL treatment solution that, by means of a simple immersion process, can remove dirt having adhered to CL surfaces, additionally can improve the lubricity of CL surfaces, and can impart persisting hydrophilicity to CL surfaces, and to provide CL treated with the CL treatment solution.

Solution to Problem

Taking the above-mentioned problems into consideration, the present inventors have made assiduous studies and, surprisingly as a result, have found that a CL treatment solution that contains, in a specific ratio, two kinds of copolymers each controlled so as to have a weight-average molecular weight falling within a specific range can solve the above-mentioned problems, and have completed the present invention.

Specifically, the gist of the present invention resides in the following [1] and [2].

[1] A contact lens treatment solution containing the following copolymer A and copolymer B in a ratio of A/B=40/1 to 5/1 (by weight):

Copolymer A: a copolymer obtained by copolymerization of a monomer (a) represented by the following formula (1) and a monomer (b) represented by the following formula (2), in which the copolymerization ratio of the monomer (a) to the monomer (b), a/b=7/3 to 9/1 (by mol), and having a weight-average molecular weight of 400,000 to 800,000; Copolymer B: a copolymer obtained by copolymerization of a monomer (a) represented by the following formula (1) and a monomer (b) represented by the following formula (2), in which the copolymerization ratio of the monomer (a) to the monomer (b), a/b=2/1 to 8/1 (by mol), and having a weight-average molecular weight of 1,000,000 to 1,500,000;

wherein R¹ represents a hydrogen atom or a methyl group;

wherein R² represents a hydrogen atom or a methyl group, and R³ represents an alkyl group having 2 to 6 carbon atoms. [2] A contact lens treated with the contact lens treatment solution of [1].

Advantageous Effects of Invention

According to the present invention, there can be provided a CL treatment solution that, by means of a simple immersion process, can remove dirt having adhered to CL surfaces, can improve the lubricity of CL surfaces, and can impart persisting hydrophilicity to CL surfaces, and also CL treated with the CL treatment solution.

DESCRIPTION OF EMBODIMENTS

Hereinunder the present invention is described in more detail.

In this description, “(meth)acrylic acid” means “acrylic acid or methacrylic acid”, and the same shall apply to other similar terms.

Also in this description, in the case where a preferred numerical range (for example, a range of content or weight-average molecular weight) is expressed in stages, the lower limit and the upper limit in each stage can be independently combined. For example, in a description of “preferably 10 to 100, more preferably 20 to 90”, “a preferred lower limit: 10” and “a more preferred upper limit: 90” can be combined to be a range “10 to 90”.

The CL treatment solution of the present invention contains the following copolymer A and copolymer B, in a ratio A/B=40/1 to 5/1 (by weight).

Copolymer A: a copolymer obtained by copolymerization of a monomer (a) represented by the following formula (1) and a monomer (b) represented by the following formula (2), in which the copolymerization ratio of the monomer (a) to the monomer (b), a/b=7/3 to 9/1 (by mol), and having a weight-average molecular weight of 400,000 to 800,000; Copolymer B: a copolymer obtained by copolymerization of a monomer (a) represented by the following formula (1) and a monomer (b) represented by the following formula (2), in which the copolymerization ratio of the monomer (a) to the monomer (b), a/b=2/1 to 8/1 (by mol), and having a weight-average molecular weight of 1,000,000 to 1,500,000;

wherein R¹ represents a hydrogen atom or a methyl group;

wherein R² represents a hydrogen atom or a methyl group, and R³ represents an alkyl group having 2 to 6 carbon atoms. [Copolymer A]

The copolymer A in the present invention is a copolymer of a monomer (a) represented by the formula (1) and a monomer (b) represented by the formula (2).

R¹ of the monomer (a) represented by the formula (1) is a hydrogen atom or a methyl group, and is preferably a methyl group from the viewpoint of raw material availability.

R² of the monomer (b) represented by the formula (2) is a hydrogen atom or a methyl group, and is preferably a methyl group from the viewpoint of storage stability of the copolymer.

R³ is an alkyl group having 2 to 6 carbon atoms. Accordingly, preferred examples of the monomer (b) include ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate, and hexyl (meth)acrylate. Especially highly effective for imparting persisting hydrophilicity to CL, R³ in the formula (2) of the monomer (b) is preferably an alkyl group having 3 to 5 carbon atoms, and above all, butyl (meth)acrylate is more preferred and butyl methacrylate is especially preferred.

In the copolymer A, the copolymerization ratio of the monomers (a) and (b) is a/b=7/3 to 9/1 (by mol). Such a range facilitates impartation of persisting hydrophilicity to CL surfaces. The copolymerization ratio of the monomers (a) and (b) in the copolymer A is preferably a/b=3/1 to 4/1 (by mol).

The copolymerization ratio of the monomers (a) and (b) in the copolymer A in the present invention and in the copolymer B to be described below means a molar ratio of the structural unit (of the following formula (3)) derived from the monomer (a) to the structural unit (of the following formula (4)) derived from the monomer (b). The copolymerization ratio generally corresponds to the ratio of the charged amount of the monomer (a) to the monomer (b) in polymerization to give the copolymer.

wherein R¹ represents a hydrogen atom or a methyl group.

wherein R² represents a hydrogen atom or a methyl group, and R³ represents an alkyl group having 2 to 6 carbon atoms.

The copolymers A and B in the present invention each contains the monomer (a)-derived structural unit (of the above formula (3)) and the monomer (b)-derived structural unit (of the above formula (4)), as described above. The copolymers A and B in the present invention may be composed of the monomer (a)-derived structural unit and the monomer (b)-derived structural unit alone, or may contain any other structural unit than these, but are preferably composed of the monomer (a)-derived structural unit and the monomer (b)-derived structural unit alone.

The weight-average molecular weight of the copolymer A in the present invention is 400,000 to 800,000, preferably 500,000 to 700,000. By controlling the weight-average molecular weight of the copolymer A to fall within the range, the effect of imparting persisting hydrophilicity to CL is enhanced.

The weight-average molecular weight of the copolymer A and the copolymer B to be described below is a polyethylene glycol-equivalent value measured through GPC (gel permeation chromatography).

The weight-average molecular weight can be measured through GPC using, for example, EcoSEC System (by Tosoh Corporation).

[Copolymer B]

The copolymer B in the present invention is a copolymer of a monomer (a) represented by the formula (1) and a monomer (b) represented by the formula (2). In the copolymer B, the copolymerization ratio of the monomers (a) and (b) is a/b=2/1 to 8/1 (by mol). Such a range facilitates impartation of persisting hydrophilicity to CL surfaces. The copolymerization ratio of the monomers (a) and (b) in the copolymer B is preferably a/b=3/1 to 4/1 (by mol).

The copolymerization ratio of the monomers (a) and (b) may be the same in the copolymer A and the copolymer B, or may differ therebetween.

The structures of the monomers (a) and (b) for use for polymerization to give the copolymer B are as described hereinabove for the copolymer A, and the preferred embodiments of R¹, R² and R³ are also the same as above. However, the kind of the monomer (a) for polymerization may be the same in the copolymers A and B or may differ therebetween, and similarly, the kind of the monomer (b) may be the same in the copolymers A and B or may differ therebetween,

The weight-average molecular weight of the copolymer B in the present invention is 1,000,000 to 1,500,000, preferably 1,100,000 to 1,300,000. By controlling the weight-average molecular weight of the copolymer B to fall within the range, the effect of imparting persisting hydrophilicity to CL is enhanced.

[Content of Copolymer a and Copolymer B]

The CL treatment solution of the present invention contains the copolymer A and the copolymer B in a ratio of A/B=40/1 to 5/1 (by weight).

When the weight ratio of the copolymer A and the copolymer B falls outside the range, for example, when the amount of the copolymer B is too small, the effect of imparting lubricity to CL surfaces and the effect of imparting persisting hydrophilicity thereto may lower, and when the amount of the copolymer B is too large, the effect of removing dirt having adhered to CL surface, the effect of imparting lubricity to CL surfaces, and the effect of imparting persisting hydrophilicity thereto may lower.

The CL treatment solution of the present invention is, from the viewpoint of enhancing the effect of imparting persisting hydrophilicity to CL surfaces, preferably such that the copolymer A and the copolymer B therein are in a ratio of A/B=35/1 to 25/1 (by weight).

Also from the viewpoint of detergency to remove protein dirt, preferably, A/B=10/1 to 5/1 (by weight).

In the present invention, the two copolymers each controlled to have a weight-average molecular weight falling within the above range are used in the ratio mentioned above, and accordingly the effect of imparting persisting hydrophilicity to CL can be attained. Though the whole picture of the principle is not as yet clarified, it is considered that the copolymer B may preferentially fix on CL surfaces to form a matrix thereon thereby playing a role of holding the copolymer A on CL surfaces.

The total content of the copolymer A and the copolymer B in the CL treatment solution of the present invention is preferably 0.01 to 5.0% by weight in the total amount of the CL treatment solution, more preferably 0.1 to 1.0% by weight. The content of 0.01 to 5.0% by weight can readily attain a sufficient persisting hydrophilicity-imparting effect, and is economical since the effect commensurate with the added amount can be attained.

[Production Method for Copolymer]

As the polymerization method for producing the copolymer A and the copolymer B in the present invention, employable is a a known method of solution polymerization, bulk polymerization, emulsion polymerization or suspension polymerization, and for example, employable is a method of radical polymerization of polymerizing the monomer (a) and the monomer (b) in a solvent in the presence of a polymerization initiator.

The initiator for polymerization may be any commonly used initiator, and for example, for radical polymerization, an aliphatic azo compound and an organic oxide can be used. Examples of the polymerization initiator include 2,2′-azobisisobutyronitrile, azobisisodimethylvaleronitrile, benzoyl peroxide, lauroyl peroxide, diisopropylperoxy dicarbonate, t-butylperoxy 2-ethylhexanoate, t-butylperoxy pivalate, t-butylperoxy diisobutyrate, and persulfates such as potassium persulfate and ammonium persulfate. Two or more kinds of these polymerization initiators may be used as mixed. Along with a polymerization initiator, a redox radical accelerator may be used as combined.

The polymerization temperature is preferably 30 to 80° C., more preferably 40 to 70° C. The polymerization time is preferably 2 to 72 hours. This is for favorably promoting polymerization. Further, for smoothly carrying out polymerization, a solvent may be used. The solvent includes water, methanol, ethanol, propanol, t-butanol, benzene, toluene, dimethylformamide, tetrahydrofuran, dioxane, chloroform, and mixed solvents of these.

[Preparation of CL Treatment Solution]

The CL treatment solution of the present invention can be prepared by mixing the above-mentioned copolymer A and copolymer B in a solvent. The solvent for use in the present invention may be arbitrarily selected from those capable of dissolving or stably dispersing the copolymer A and the copolymer B and having few influences on CL. Preferred examples of such solvents include water such as pure water, and solvents that have a property of misciblity with water in any ratio, such as ethanol, isopropanol, ethylene glycol, propylene glycol or glycerin, and mixed solvents of these.

In addition to the copolymer A and the copolymer B, a surfactant is preferably incorporated in the CL treatment solution of the present invention for enhancing detergency and the like. The surfactant can be selected in any desired manner from those not detracting from the advantageous effects of the present invention.

Examples of such surfactants include anionic surfactants such as polyoxyethylene alkyl ether sulfates, polyoxyethylene fatty acid amide ether sulfates, N-acyl-N-methyltaurinates, alkyl sarcosinates, alkylamide sulfosuccinates, alkyl sulfates, dialkyl sulfosuccinates, and N-alkyl-N,N-dimethyloxides; nonionic surfactants such as sorbitan fatty acid esters, and polyoxyethylene hydrogenated castor oil; and ampholytic surfactants such as alkyldimethylaminoacetic acid betaine, 2-alkyl-N-carboxymethyl-N-hydroxyethylimidazolium betaine, alkylamidepropyl betaine, and alkylaminodiacetates. Above all, from the viewpoint of high detergency, few influences on eyes and solution stability, anionic surfactants are preferred, and polyoxyethylene alkyl ether sulfates or polyoxyethylene fatty acid amide ether sulfates are especially preferably used. Specifically, they include polyoxyethylene coconut oil fatty acid monoethanolamide sulfates, lauric acid amide ether sulfate ester salts, myristic acid amide ether sulfate ester salts, and mixtures thereof.

The content of the surfactant in the CL treatment solution of the present invention is preferably 0.01 to 5% by weight in the overall amount of the CL treatment solution, more preferably 0.1 to 2.0% by weight. When the content is 0.01 to 5.0% by weight, sufficient detergency can be attained.

In addition to the copolymer A and the copolymer B, the CL treatment solution of the present invention preferably contains a hydrolase for the purpose of decomposing dirt on CL. For the hydrolase, any generally-known hydrolase can be appropriately selected and used within a range not overstepping the object of the present invention. Specifically, the hydrolase can be arbitrarily selected from those capable decomposing tough dirt that could not be removed by surfactant, without having any influence on the properties of CL.

In particular, tear-derived dirt ingredients include glycoproteins such as mucin, proteins such as lysozyme and lipids, and hydrolases having an effect of decomposing these to facilitate removal of dirt on CL are preferably used. Examples of these hydrolases include proteases such as “Bioprase” (by Nagase ChemteX Corporation), “Protease CL-15” (by Nagase ChemteX Corporation), “Clear Lens Pro” (by Novozymes Corporation), “Esperase CLC” (by Novozymes Corporation); lipolytic enzymes such as lipase, phospholipase A, phospholipase B, phospholipase C, phospholipase D and cholesterol esterase; carbohydrate chain degrading enzymes such as α-amylase, endoglycosidase D, endo-ß-galactosidase, ß-galactosidase, cellulase, and dextranase.

The content ratio of the hydrolase in the CL treatment solution of the present invention is preferably 10⁻¹⁰% by weight to 1% by weight, more preferably 10⁻⁶% by weight to 0.1% by weight in the entire amount of the CL treatment solution. When the content ratio is 10⁻¹⁰% by weight to 1% by weight, sufficient detergency can readily be attained.

In addition to the copolymers A and B, the CL treatment solution of the present invention preferably contains a buffering solution for the purpose of maintaining the pH of the solution. The buffering solution can be arbitrarily selected from any one not detracting from the advantageous effects of the present invention, and preferred examples thereof include buffering solutions that are prepared using any of hydrochloric acid, acetic acid, citric acid, boric acid, phosphoric acid, sodium hydroxide, potassium hydroxide, triethanolamine, tris(hydroxymethyl)aminomethane, salts thereof, and mixtures thereof according to an ordinary method.

In addition to the copolymers A and B, the CL treatment solution of the present invention may contain a chelating agent for the purpose of stabilizing the solution and removing metal salts on CL surfaces. The chelating agent can be arbitrarily selected form those not detracting from the advantageous effects of the present invention, and preferred examples thereof include polycarboxylic acids such as citric acid, ethylenediaminetetraacetic acid and cyclohexadiamine tetraacetic acid, and alkali metal salts thereof, and mixtures thereof.

In addition to the copolymers A and B, the CL treatment solution of the present invention may contain an inorganic salt for the purpose of reducing influences on eyes and for tonicity adjustment. The inorganic salt can be arbitrarily selected from any one not overstepping the object of the present invention, and preferred examples thereof include sodium chloride, potassium chloride, magnesium chloride and mixtures thereof.

In addition to the copolymers A and B, a water-soluble polymer compound may be added to the CL treatment solution of the present invention for the purpose of controlling the viscosity of the solution. The water-soluble polymer compound can be arbitrarily selected from those not detracting from the function of the present invention, and examples thereof include polyethylene glycol, polypropylene glycol, polyvinyl alcohol, polyvinyl pyrrolidone, carboxymethyl cellulose, hydroxyethyl cellulose, hydroxypropylmethyl cellulose, polyethylene oxide-polypropylene oxide block copolymer, maleic anhydride-methyl vinyl ether copolymer, and mixtures thereof.

The CL treatment solution of the present invention may contain a preservative for the purpose of preventing growth of bacteria. For example, as the preservative, chlorobutanol, benzalkonium chloride, thimerosal, chlorohexidine gluconate, paraoxybenzoate, and polyhexamethylene biguanide are preferably added.

Regarding use of the CL treatment solution of the present invention, for example, a method of immersing CL in the CL treatment solution or bringing CL into contact with the CL treatment solution is employable. Subsequently, before wearing them, preferably, CL are rinsed with water, a physiological saline solution and/or a cleaning solution. In that manner, by using the CL treatment solution, dirt having adhered to CL surfaces can be removed, the lubricity of CL treatment can be bettered, and further, persisting hydrophilicity can be given to CL to prevent adhesion of dirt of proteins, lipids and the like to CL.

In addition, according to the method, CL treated with the CL treatment solution of the present invention can be readily obtained.

The CL treatment solution of the present invention is favorably used for any of hard contact lenses (HCL), soft contact lenses (SCL), and other generally-known CL to give CL treated with the CL treatment solution of the present invention in a simple manner.

EXAMPLES

Hereinunder the present invention is described in more detail with reference to Examples, to which, however, the present invention is not limited.

<Synthesis of Copolymer>

For synthesis of copolymers for use in Examples and Comparative Examples, five types of copolymers, that is, a copolymer 1 of the copolymer A, copolymers 2 and 3 of the copolymers B, and copolymers 4 and 5 of other copolymers than the copolymers A and B were synthesized.

Synthesis Example 1

19.4 g of 2-methacryloyloxyethylphosphorylcholine (hereinafter expressed as MPC), and 2.2 g of butyl methacrylate (hereinafter expressed as BMA) (monomer composition molar ratio: MPC/BMA=8/2) were weighed in a glass flask for polymerization, and as a polymerization initiator, 86 mg of 2,2′-azobisisobutyronitrile (hereinafter expressed as AIBN), and as polymerization solvents, 39.2 g of pure water and 39.2 g of ethanol were added thereto. The reactor was fully purged with nitrogen, and then heated at 60° C. for 5 hours for polymerization. The resultant reaction liquid was cooled with ice, and dropwise put into diethyl ether to precipitate the polymer. The precipitate was filtered out, washed with diethyl ether and then dried in vacuum to give a white solid copolymer 1.

The weight-average molecular weight of the resultant copolymer 1 was 600,000 as a polyethylene glycol-equivalent one measured through gel permeation chromatography (hereinafter expressed as GPC).

Synthesis Example 2

21.5 g of MPC and 2.9 g of BMA (monomer composition molar ratio: MPC/BMA=7/2) were weighed in a glass flask for polymerization, and as a polymerization initiator, 96 mg of 2,2′-azobisisobutyronitrile (hereinafter expressed as AIBN), and as polymerization solvents, 37.8 g of pure water and 37.8 g of ethanol were added thereto. The reactor was fully purged with nitrogen, and then heated at 50° C. for 7 hours for polymerization. The resultant reaction liquid was cooled with ice, and dropwise put into diethyl ether to precipitate the polymer. The precipitate was filtered out, washed with diethyl ether and then dried in vacuum to give a white solid copolymer 2.

The weight-average molecular weight of the resultant copolymer 2 was 1,210,000 as a polyethylene glycol-equivalent one measured through GPC.

Synthesis Example 3

21.8 g of MPC and 2.6 g of BMA (monomer composition molar ratio: MPC/BMA=8/2) were weighed in a glass flask for polymerization, and as a polymerization initiator, 96 mg of 2,2′-azobisisobutyronitrile (hereinafter expressed as AIBN), and as polymerization solvents, 39.3 g of pure water and 36.3 g of ethanol were added thereto. The reactor was fully purged with nitrogen, and then heated at 50° C. for 7 hours for polymerization. The resultant reaction liquid was cooled with ice, and dropwise put into diethyl ether to precipitate the polymer. The precipitate was filtered out, washed with diethyl ether and then dried in vacuum to give a white solid copolymer 3.

The weight-average molecular weight of the resultant copolymer 3 was 1,240,000 as a polyethylene glycol-equivalent one measured through gel permeation chromatography (hereinafter expressed as GPC).

Synthesis Example 4

4.7 g of MPC and 5.3 g of BMA (monomer composition molar ratio: MPC/BMA=3/7) were weighed in a glass flask for polymerization, and as a polymerization initiator, 244 mg of 2,2′-azobisisobutyronitrile (hereinafter expressed as AIBN), and as a polymerization solvent, 89.8 g of ethanol were added thereto. The reactor was fully purged with nitrogen, and then heated at 60° C. for 7 hours for polymerization. The resultant reaction liquid was cooled with ice, and dropwise put into diethyl ether to precipitate the polymer. The precipitate was filtered out, washed with diethyl ether and then dried in vacuum to give a white solid copolymer 4.

The weight-average molecular weight of the resultant copolymer 4 was 93,000 as a polyethylene glycol-equivalent one measured through GPC.

Synthesis Example 5

11.7 g of MPC, and 3.3 g of stearyl methacrylate (hereinafter expressed as SMA) (monomer composition molar ratio: MPC/SMA=8/2) were weighed in a glass flask for polymerization, and as a polymerization initiator, 433 mg of 2,2′-azobisisobutyronitrile (hereinafter expressed as AIBN), and as a polymerization solvent, 84.6 g of ethanol were added thereto. The reactor was fully purged with nitrogen, and then heated at 60° C. for 6 hours for polymerization. The resultant reaction liquid was cooled with ice, and dropwise put into diethyl ether to precipitate the polymer. The precipitate was filtered out, washed with diethyl ether and then dried in vacuum to give a white solid copolymer 5.

The weight-average molecular weight of the copolymer 5 was 43,000 as a polyethylene glycol-equivalent one measured through GPC.

<GPC Measurement>

The copolymers of Synthesis Examples 1 to 5 were subjected to GPC under the following conditions.

GPC System: High-Performance Liquid Chromatography System CCP & 8020 Series (by Tosoh Corporation).

Columns: Shodex OHpak SB-802.5HQ (by Showa Denko KK) and SB-806HQ (by Showa Denko KK) were connected in series.

Developing solvent: 20 mM sodium phosphate buffer (pH 7.4).

Detector: Differential refractive index detector, UV detector (wavelength 210 nm).

Molecular weight standard: EasiVial PEG/PEO (by Agilent Technologies Corporation).

Flow rate: 0.5 mL/min.

Column temperature: 45° C.

Sample: The resultant copolymer was diluted with the developing solvent to have a final concentration of 0.1% by weight.

TABLE 1 Synthesis Synthesis Synthesis Synthesis Synthesis Example 1 Example 2 Example 3 Example 4 Example 5 Copolymer 1 Copolymer 2 Copolymer 3 Copolymer 4 Copolymer 5 Monomer Monomer (a) MPC 8 7 8 3 8 Composition Monomer (b) BMA 2 2 2 7 — (molar ratio) — SMA — — — — 2 Weight-Average Molecular Weight 600 1,210 1,240 93 43 (×10³)

Example 1

The copolymer 1 of copolymer A, the copolymer 2 of copolymer B, and other components were blended in a ratio shown in Table 3 to prepare a CL treatment solution. The CL treatment solution was evaluated as follows. The results are shown in Table 3.

(I) Detergency Evaluation (Protein Dirt)

In a physiological saline solution containing 0.39% by weight of bovine serum albumin, 0.16% by weight of human γ-globulin, 0.12% by weight of egg-white lysozyme and 0.10% by weight of porcine gastric mucin, contact lenses (Seed Super Hi-O₂, by Seed Co., Ltd.) were treated at 60° C. for 2 hours to be contaminated. The lenses were immersed in the CL treatment solution for 4 hours, then rinsed with tap water, and the protein on the lenses were extracted with an aqueous 1% sodium dodecyl sulfate solution, and the extracted amount of the protein was quantified with a micro BCA kit (by Thermo Fisher Scientific KK) (C_(ps)).

Further, protein quantification was carried out in the same manner as above except that physiological saline water was used in place of the CL treatment solution (C_(p0)). According to the following mathematical expression (1), the protein removal ratio was calculated, and the CL treatment solution was evaluated as C: less than 50%, B: 50% or more and less than 70%, and A: 70% or more.

$\begin{matrix} {{{Protein}\mspace{14mu}{Removal}\mspace{14mu}{Ratio}} = {\frac{C_{p\; 0} - C_{ps}}{C_{p\; 0}} \times 100\mspace{11mu}(\%)}} & (1) \end{matrix}$ (II) Detergency Evaluation (Lipid Dirt)

In a physiological saline solution in which 0.60% by weight of oleic acid, 0.60% by weight of linolic acid, 0.60% by weight of palmitic acid, 8.12% by weight of tripalmitin, 2.00% by weight of cetyl alcohol, 8.12% by weight of cetyl myristate, 0.80% by weight of cholesterol, 0.80% by weight of cholesterol palmitate, and 28.36% by weight of egg-yolk lecithin had been emulsified, contact lenses (Seed Super Hi-O₂, by Seed Co., Ltd.) were treated at 35° C. for 4 hours to be contaminated. The lenses were immersed in the CL treatment solution for 4 hours, then rinsed with tap water, and the lipid on the lenses were extracted with a mixed solvent of chloroform/methanol=1/1 (by volume), and the solvent was evaporated away. The remaining lipid was quantified according to a sulfuric acid-vanillin method (C_(ls)).

Further, lipid quantification was carried out in the same manner as above except that physiological saline water was used in place of the CL treatment solution (C_(l0)). According to the following mathematical expression (2), the lipid removal ratio was calculated, and the CL treatment solution was evaluated as C: less than 0%, B: 0% or more and less than 40%, and A: 40% or more.

$\begin{matrix} {{{Lipid}\mspace{14mu}{Removal}\mspace{14mu}{Ratio}} = {\frac{C_{10} - C_{ls}}{C_{10}} \times 100\mspace{11mu}(\%)}} & (2) \end{matrix}$ (III) Lubricity

An acrylic board was immersed and treated overnight in the CL treatment solution. This was rinsed with tap water and then dried (for simulation of a state before wearing). Further, the acrylic board was immersed in physiological saline water for 3 hours, then dried (for simulation of a state after wearing), and the coefficient of kinematic friction thereof was measured using a friction sensitivity tester (KES-SE, Kato Tech Co., Ltd.) fitted with a silicon rubber probe (μ_(s)).

Further, the coefficient of kinematic friction was measured in the same manner as above except that tap water was used in place of the CL treatment solution (μ₀). According to the following mathematical expression (3), the lubrication ratio (initial stage) was calculated, and the CL treatment solution was evaluated as C: less than 0%, B: 0% or more and less than 40%, and A: 40% or more.

$\begin{matrix} {{{Lubrication}\mspace{14mu}{ratio}} = {\frac{\mu_{0}\mu_{s}}{\mu_{0}} \times 100\mspace{11mu}(\%)}} & (3) \end{matrix}$ (IV) Persisting Hydrophilicity [1] Contact lenses (Hard EX1, by Seed Co., Ltd.) were rinsed with tap water, and immersed and treated overnight in the CL treatment solution. These were rinsed with physiological saline water, and then BUT thereof was measured (W_(is)). BUT means a tear break up time, a time (second) taken just after CL were drawn up from physiological saline water and then the CL convex surfaces were observed before no liquid chopping was from CL. [2] Further, the CL were put into a 12-well plate and immersed in 2 mL of physiological saline water, and shaken for 3 hours (for simulation of a state after wearing). BUT of the CL was measured in the same manner as above (W_(fs)). [3] Further, in the same manner as in the above [1] except that physiological saline water was used in place of the CL treatment solution in the above [1], BUT before immersion for 6 hours in physiological saline water was measured (W_(i0)). [4] According to the following mathematical expressions (4) and (5), the hydrophilicity degree before and after immersion for 6 hours in physiological saline water was calculated, and the CL treatment solution before immersion was evaluated as C: less than 0, B: 0 or more and less than 1, and A: 1 or more, and after immersion, as C: less than 0, B: 0 or more and less than 0.9, and A: 0.9 or more. Further, based on these evaluation data, the persisting hydrophilicity was judged according to Table 2.

$\begin{matrix} {{{Hydrophilicity}\mspace{14mu}{Degree}\mspace{11mu}\left( {{before}\mspace{14mu}{immersion}} \right)} = {\log_{10}\frac{W_{is}}{W_{10}}}} & (4) \\ {{{Hydrophilicity}\mspace{14mu}{Degree}\mspace{11mu}\left( {{after}\mspace{14mu}{immersion}} \right)} = {\log_{10}\frac{W_{fs}}{W_{10}}}} & (5) \end{matrix}$

TABLE 2 Hydrophilicity Degree (before immersion) A B C Hydrophilicity Degree A S A B (after immersion) B A B C C B C C

Examples 2 to 4

CL treatment solutions each having a composition shown in Table 3 were prepared and evaluated in the same manner as in Example 1. The results are shown in Table 3.

Comparative Examples 1 to 6

CL treatment solutions each having a composition shown in Table 4 were prepared and evaluated in the same manner as in Example 1. The results are shown in Table 4.

TABLE 3 Example 1 2 3 4 CL Copolymer A Copolymer 1 0.3  0.3  0.3  0.3  Treatment Copolymer B Copolymer 2 0.01 0.01 — — Solution Copolymer 3 — — 0.01 0.05 (% by weight) Other Copolymer 4 — — — — Copolymer Copolymer 5 — — — — Other Glycerin 5   Component PG 10   SPCS 1.4 TLS  0.55 CLP 0.02 — —  0.007 ECLC —  0.007  0.007 — Boric Acid 1.5 NaOH  0.56 EDTA 0.1 Water balance Copolymer A/Copolymer B (by mass) 30/1 30/1 30/1 6/1 Evaluation Results Detergency A [73%] A [80%] A [86%] A [87%] (protein) *1 Detergency A [47%] A [47%] A [50%] A [57%] (lipid) *2 Lubricity*3 A [40%] A [40%] A [40%] A [40%] Persisting S [1.3/0.9] S [1.3/0.9] S [1.3/0.9] A [1.4/0.7] Hydrophilicity*4 *1 Protein removal ratio is parenthesized. *2 Lipid removal ratio is parenthesized. *3 Lubrication ratio is parenthesized. *4 [Hydrophilicity Degree (before immersion)/Hydrophilicity Degree (after immersion)]

Abbreviations used in Table 3 are as follows.

PG: propylene glycol

SPCS: sodium PEG-4 cocamide sulfate (polyoxyethylene coconut oil fatty acid monoethanolamide sodium sulfate)

TLS: TEA-laureth sulfate (polyoxyethylene lauryl ether sulfate triethanolamine)

CLP: Clear Lens Pro (by Novozymes Corporation)

SCLC: Esperase CLC (by Novozymes Corporation)

NaOH: sodium hydroxide

EDTA: ethylenediaminetetraacetic acid

TABLE 4 Comparative Example 1 2 3 4 5 6 CL Copolymer A Copolymer 1 0.3 0.5 0.3 0.3 0.3 0.3 Treatment Copolymer B Copolymer 2 — —  0.005 0.3 — — Solution Copolymer 3 — — — — — — (% by weight) Other Copolymer 4 — — — —  0.01 — Copolymer Copolymer 5 — — — — —  0.01 Other Glycerin 5   Component PG 10    SPCS 1.4  TLS 0.55 CLP 0.02 ECLC — Boric Acid 1.5  NaOH 0.56 EDTA 0.1  Water balance Copolymer A/Copolymer B (by mass) 1/0 1/0 60/1 1/1 — — Evaluation Results Detergency A [75%] A [74%] A [90%] B [68%] B [66%] B [67%] (protein) Detergency B [35%] B [37%] A [42%] B [28%] B [31%] B [34%] (lipid) Lubricity B [30%] B [30%] B [30%] B [30%] B [10%] B [30%] Persisting A [1.3/0.7] B [0.8/0.6] A [1.4/0.8] B [0.7/0.8] B [0.7/0.6] B [0.7/0.7] Hydrophilicity *1 Protein removal ratio is parenthesized. *2 Lipid removal ratio is parenthesized. *3 Lubrication ratio is parenthesized. *4 [Hydrophilicity Degree (before immersion)/ Hydrophilicity Degree (after immersion)]

Abbreviations used in Table 4 are as follows.

PG: propylene glycol

SPCS: sodium PEG-4 cocamide sulfate (polyoxyethylene coconut oil fatty acid monoethanolamide sodium sulfate)

TLS: TEA-laureth sulfate (polyoxyethylene lauryl ether sulfate triethanolamine)

CLP: Clear Lens Pro (by Novozymes Corporation)

ECLC: Esperase CLC (by Novozymes Corporation)

NaOH: sodium hydroxide

EDTA: ethylene diaminetetraacetic acid

The results in Examples and Comparative Examples reveal the following.

Not containing a high-molecular-weight copolymer, the copolymer B, Comparative Example 1 was inferior to Examples in point of lubricity and persisting hydrophilicity. Comparative Example 2 was so formulated as to have an increased amount of the copolymer A in place of containing the copolymer B, but was also inferior to Examples in point of lubricity and persisting hydrophilicity. From these, it is known that for achieving lubricity and persisting hydrophilicity, it is necessary to add a high-molecular-weight component but not to merely increase the amount of the copolymer A.

Comparative Example 3 was so formulated that the content of the copolymer B therein was a half in Examples, but was inferior to Examples in point of lubricity and persisting hydrophilicity. Contrary to this, Comparative Example 4 was so formulated that the content of the copolymer B was excessively increased, but was also inferior to Examples in point of lubricity and persisting hydrophilicity. From these, it is known that the amount of the copolymer B needs to fall within the concentration range defined in this specification.

Comparative Example 5 used the copolymer 4 falling outside the scope of the present invention, in place of the copolymer B. In the copolymer 4, the magnitude relationship of the copolymerization ratio of the monomers (a) and (b) was reversed relative to the copolymers 2 and 3 falling within the scope of the present invention, and in addition, the weight-average molecular weight of the copolymer 4 was small not falling within the scope of the present invention. Comparative Example 5 was also inferior to Examples in point of lubricity and persisting hydrophilicity. From these, it is known that the copolymer falling within the scope defined in this specification needs to be used as a copolymer B.

Further, Comparative Example 6 used the copolymer 5 falling outside the scope of the present invention, in place of the copolymer B. The copolymer used SMA having a longer chain alky group than that in BMA as the monomer (b), relative to the copolymer 3 falling within the scope of the present invention, and in addition, the weight-average molecular weight thereof was small not falling within the scope of the present invention. Comparative Example 6 was also inferior to Examples in point of lubricity and persisting hydrophilicity. From these, it is known that the copolymer falling within the scope defined in this specification needs to be used.

On the other hand, Examples were confirmed to achieve more excellent effects than Comparative Examples in point of all the evaluation items of detergency (protein), detergency (lipid), lubricity and persisting hydrophilicity. Namely, the present invention can provide a CL treatment solution capable of removing dirt having adhered to CL surfaces, capable of improving lubricity of CL surfaces and capable of imparting persisting hydrophilicity to CL surfaces, by simple immersion treatment. 

The invention claimed is:
 1. A contact lens treatment solution comprising copolymer A and copolymer B in a ratio of A/B=40/1 to 5/1 by weight, wherein the copolymer A is obtained by copolymerization of a first monomer (a) represented by formula (1) and a first monomer (b) represented by formula (2), in which a first copolymerization ratio of the first monomer (a) to the first monomer (b) is 7/3 to 9/1 by mol, the copolymer A having a weight-average molecular weight of 400,000 to 800,000, wherein the copolymer B is obtained by copolymerization of a second monomer (a) represented by the formula (1) and a second monomer (b) represented by the formula (2), in which a second copolymerization ratio of the second monomer (a) to the second monomer (b) is 2/1 to 8/1 by mol, the copolymer B having a weight-average molecular weight of 1,000,000 to 1,500,000,

wherein R¹ represents a hydrogen atom or a methyl group,

wherein R² represents a hydrogen atom or a methyl group, and R³ represents an alkyl group having 2 to 6 carbon atoms.
 2. The contact lens treatment solution of claim 1, wherein: the first monomer (a) and the second monomer (a) are the same.
 3. The contact lens treatment solution of claim 1, wherein: the first monomer (a) and the second monomer (a) are different.
 4. The contact lens treatment solution of claim 1, wherein: the first monomer (b) and the second monomer (b) are the same.
 5. The contact lens treatment solution of claim 1, wherein: the first monomer (b) and the second monomer (b) are different.
 6. The contact lens treatment solution of claim 1, wherein: the first copolymerization ratio of the first monomer (a) to the first monomer (b) is 3/1 to 4/1 by mol.
 7. The contact lens treatment solution of claim 1, wherein: the copolymer A has a weight-average molecular weight of 500,000 to 700,000.
 8. The contact lens treatment solution of claim 1, wherein: the second copolymerization ratio of the second monomer (a) to the second monomer (b) is 3/1 to 4/1 by mol.
 9. The contact lens treatment solution of claim 1, wherein: the copolymer B has a weight-average molecular weight of 1,100,000 to 1,300,000.
 10. The contact lens treatment solution of claim 9, wherein: the copolymer B has a weight-average molecular weight of 1,200,000 to 1,250,000.
 11. The contact lens treatment solution of claim 1, wherein: the ratio of A/B is 35/1 to 25/1 by weight.
 12. The contact lens treatment solution of claim 1, wherein: the ratio of A/B is 10/1 to 5/1 by weight.
 13. The contact lens treatment solution of claim 1, wherein: a total amount of the copolymer A and the copolymer B in the contact lens treatment solution is 0.01% to 5.0% by weight.
 14. The contact lens treatment solution of claim 13, wherein: the total amount of the copolymer A and the copolymer B in the contact lens treatment solution is 0.1% to 1.0% by weight.
 15. The contact lens treatment solution of claim 1, wherein: R¹ represents a methyl group, R² represents a methyl group, and R³ represents an alkyl group having 3 to 5 carbon atoms.
 16. The contact lens treatment solution of claim 1, wherein: the first monomer (b) is ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate or hexyl (meth)acrylate, and the second monomer (b) is independently ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate or hexyl (meth)acrylate.
 17. The contact lens treatment solution of claim 1, further comprising at least one of a surfactant, a hydrolase, a buffer, a chelating agent, an inorganic salt, a water-soluble polymer compound or a preservative. 